ZYTROL-7500

Zytrol-7500 is a speciality water borne adhesive for wet lamination and packing. It is multifunctional in the sense that it can give very good adhesion to polyester, BOPP, PVC films on Pigmented and Metallic Inks and it is found to retain adhesion even under conditions of direct sun light and high humidity.
Features

Use of  speciality Emulsion Polymerization.

Softer Polymer.

New Special Chemistry.

Excellent reemulsification.

Good flow and leveling.

Multifunctional Adhesive.

Finer Particle Size.

 Benefits

Finer particle size leading to improved adhesive strength and retention of adhesion.Gives good flexibility and retentivity of adhesion on packing material. Prevents channeling.

Faster Curing Post Lamination. Reduces in-process inventory.

Easy for cleaning rollers and application machinery and improved machine and labour productivity.

Ensures uniform film properties, exhibits better gloss and clarity.

Reduced Inventory of Multiple Product.

Better Coverage (30%-40%), compared to contemporary adhesives and hence reduced cost.

Appearance                  :    Milky White
Solids content               :    43 ± 2%
pH                              :     8 ± 0.5
Viscosity                      :    9000± 3000 cps

Zytrol-7500 should be applied by normal application procedure for adhesives.

* Zytrol-7500 is very easy to handle and normal departmental procedures should be    followed.

* Store at ambient temperature.

* After each withdrawal from the container, always ensure to close the cap tightly.

In case of lower viscosity, we can provide an additive which can be added at 0.1 to 0.5% level increase the viscosity. the additive will be needed only under unusual conditions of application or storage.

ZYPOL-25

Zypol-25 is a New Generation Polymer for Bonding of Polyester Fiber  for Wadding/Batting and Back Coating of Non-Woven Fabrics and woven fabrics including fur fabric. It provides excellent adhesion to polyester fiber and prevents migration. The small particle size of the polymer helps in better penetration and provides multi-point bonding even in the inner layers of the substrates. It is possible to reduce the dosage level by about 30%-35% compared to self cross-linking acrylic resins.
Features

Structure with perfect combination of polar and non-polar groups.Smaller particle size & hence better penetration.

Excellent cohesive & adhesive strength.

Lower film forming temperature.

 

 Benefits

Exceptional adhesion to Polyester Surface

Softer feel & Improved Resiliency of Wadding/Non-wovens.

Stronger bonding at even lower dosage levels. Better final product.

Curing at lower temperature i.e. 110 – 120 degree C – Saving of energy.

Appearance          :  Translucent Liquid
Diluent                :   Water
Solid content        :    25 ± 1.5%
pH                      :    6.5 to 7.5
Viscosity              :   5-10 CP
Nature                 :   Anionic

It is easy to prepare solution of ZYPOL-25. Following procedure may be adopted for making 10% solution :

ZYPOL-25 : 40 kg
Water (Demineralized water or Soft water with low total dissolved solids) : 60 kg
Total Wt. : 100 kg
Note: Solid content of recipe is  40  x  0.25 : 10.00%
Total Weight
  1. Take 60 parts of the total water used in the recipe.
  2. Addition of 40 parts of  ZYPOL-25 should be done slowly in 5-10 minutes.
  3. Mix thoroughly. Adjust the concentration and start spraying on the substrate.

* Keep the carboys of  ZYPOL-25 in cool shade.
* Do not store above 40oC or in direct sun.
* Stable for 3-4 months at room temperature.

ZYPOL

Zypol is a New Generation polymer for Bonding of Polyester Fiber  for Wadding/Batting and Back Coating of Non-Woven Fabrics and woven fabrics. It provides excellent adhesion to polyester fiber and prevents migration. The small  particle size of the polymer helps in better penetration and provides multi-point bonding even in the inner layers of the substrates. It is possible to reduce the dosage level by about 30%-35% compared to self cross-linking acrylic resins.
Features

Structure with perfect combination of polar and non-polar groups.Smaller particle size & hence better penetration.

Excellent cohesive & adhesive strength.

Lower film forming temperature.

 

 Benefits

Exceptional adhesion to Polyester Surface

Softer feel & Improved Resiliency of Wadding/Non-wovens.

Stronger bonding at even lower dosage levels. Better final product.

Curing at lower temperature i.e. 110 – 120 degree C – Saving of energy.

Appearance         :   Solid Granules
Diluent                :   Water
Solid content        :   98 ± 2%
Nature                 :   Anionic

It is easy to prepare solution of ZYPOL. Following procedure may be adopted for making 10% solution :

ZYPOL : 10 kg
Water (Demineralized water or Soft water with low total dissolved solids) : 90 kg
Total Wt. : 100 kg
Note: Solid content of recipe is  Solid  x  100 : 10.00%
Total Weight
  1. Take 70 parts of water used in the recipe. Start heating and bring it close to boiling.
  2. Addition of 10 parts of  ZYPOL should be spread over 20 – 30 minutes after the temperature reaches
    90 degree C. This ensures easy solubilization. Do not add all the powder at one time.
  3. Heat further for 30 – 60 minutes to dissolve ZYPOL completely.
  4. Part of water, which evaporated during heating, should be replaced by adding equivalent amount of  water.
  5. Also add the remaining 20 parts of the water. This addition of water will bring down the temperature  to 50 – 55 degree C.
  6. Allow it to cool to 30 – 35 degree C. Adjust the concentration to desired level. Start spraying on the substrate.

    * Keep the bags of  ZYPOL in cool shade.
    * Do not store above 40oC or in direct sun.

    In case the bags are open and are intended to be stored for a longer time, ensure to tie and seal the mouth to avoid moisture contact.